BITUSEAL 1000

 

DESCRIPTION
BITUSEAL 1000  self adhesive membranes are produced with a special multi-layer design with a glasfiber reinforcement which is impregnated and coated on both sides with a uniquely formulated plastomeric bitumen compound, which provides high adhesive properties. BITUMAT 1000 is covered on its top surface with a translucent polyethylene foil and on the under side with a siliconised release paper. This combination provides instant adhesion with high tear and puncture resistance and improved tensile strength. A top surfacing of polypropylene film is also available. BITUMAT 1000 DSA with double sided adhesive finish is also available for special applications. 

USES
BITUSEAL 1000  is the ideal membrane for dam proofing foundations, bridges, viaducts, and tunnels. It is recommended for use under composition shingles and roof tiles as a protective shield against water and ice. Strips of various widths are used extensively in road design and construction.

OUTSTANDING FEATURES
· Self adhesive
- Reinforced.
- Easy to apply                                    

INSTALLATION TOOLS REQUIRED
Knife, Measuring tape, Marking string, Small roller, Gloves.

APPLICATION
The surface to receive BITUSEAL 1000 should be smooth, dry, free from dust and dirt. The surface should be primed thoroughly with BITUMAT primer BITUSEAL 1000 is installed by progressively pealing off the release paper and unrolling the membrane along with it. The membranes, particularly at the overlaps should be firmly pressed down to ensure a good seal. For details of installation methods and flashing requirements, consult the relevant BITUMAT Design and Installation Manual.            


COVERAGE RATE

For flat areas

 

                             1.13 M2/M2 per layer

For 30 cm. girth flashing

0.35 M2/Mt/ length

Average wastage

3 - 5%
 

 

 

 

QUALITY CONTROL
In In addition to stringent regular tests by BITUMAT laboratory, our products are tested by Bureau Veritas & SOCOTEC, Paris, France.


 TECHNICAL DATA
 

Property

Result

Test Method

1.

Softening point 0C

115

ASTM D-36

2.

Penetration,                            
 @ 250C, dmm                            
@ 46 0C, dmm


70 + 10
110

ASTM D-5

3.

Low temperature flexibility, (cold bend @ -15 0C for 8 days)

-20

ASTM D-5147

4.

Tensile strength, N/5 cm                
Longitudinal Transverse

 400 (5.33 N/mm2)
300 (4.0 N/mm2)

ASTM D-5147

5.

Elongation % @ break %

>2000 

ASTM D-5147

6.

Lap joint strength N/5cm
LongitudinalTransverse

400
300

CGSB-37-GP-56M UEAtc

7.

Tear resistance, KN/m 
Longitudinal  Tnsverse

26.83 (150ibf/in) 
32.20 (180 ibf/in)

ASTM D-5147

8.

Puncture Resistance, Kg

32.30

ASTM E 154.UEAtc 
5.1.9 UEAtc 5.4.1

9.

Water Absorption, % Wt (672 hrs @ 23 0C)

<0.08

 ASTM D-5147

10.

Water Vapour Transmission, g/M2/24 hrs

<0.2 impermiable

ASTM E-96 procedure E    
37.8 0C at 96% RH

11.

Adhesion Strength,  N/mm                        
To primed deck                       
To self

 
3.11
3.11

ASTM D-1000

12.

Impermiability Of welded seams to water presssure.

Absolutely impermiable

UEAtc guidelines.

13.

Resistance To Aging & U.V (Weather O-meter 2000hrs)

Pass

ASTM G53; UNI 8202


GENERAL DATA
 Roll length

                                

20, 25 or 30 Mt.

Roll width

1 Mt.

Nominal Thickness

1.5, 1.8 mm

Nominal weight             
Reinforcement

  1.5 Kg/M2 .  
 50 - 60 gsm glasfiber mat

The data listed above is subject to the tolerance limits of UEAtc specifications


The information given in this Technical Sheet is to the best of our knowledge based on laboratory tests and practical experience. However, as the product is often used under conditions beyond our control, we cannot guarantee but the product itself.